Welcome to episode 12 of the Six Lessons podcast.
00:00:30.446 --> 00:00:34.250
Today we're going to be talking about a topic near and dear to my heart.
00:00:34.384 --> 00:00:35.918
Resin coating.
00:00:35.918 --> 00:00:47.263
Resin coating is a concept that doesn't get as much respect as it should in the world of adhesive dentistry, all of the products that we use are resin based.
00:00:47.631 --> 00:00:50.766
The resin idea is a polymerized molecule.
00:00:50.766 --> 00:00:55.371
Resins can be very stiff or they can be very flexible.
00:00:55.371 --> 00:00:59.475
For example, soft contact lenses that has a monomer called Hema.
00:00:59.842 --> 00:01:02.778
The Hema is a water loving molecule.
00:01:02.778 --> 00:01:07.751
It's very small, so it's very flexible, but it also adapts well with water.
00:01:07.783 --> 00:01:19.128
Now, harder plastics like these lenses of my glasses, they have a polymerization that is much more complex and it does not like water at all.
00:01:19.128 --> 00:01:21.731
So that's a hydrophobic situation.
00:01:21.731 --> 00:01:27.871
In the composites we use, the resins have a combination of hydrophilic and hydrophobic.
00:01:27.871 --> 00:01:30.039
In the dental bonding systems.
00:01:30.039 --> 00:01:38.981
And the dental bonding systems have to connect to hydrophobic resins that are in what we call the restorative composite aspect.
00:01:38.981 --> 00:01:55.932
But in between the dental bonding system and the restorative materials that we use, which are composites, we need to understand that there has been a tremendous amount of experimentation and that experimentation has been both in the bonding systems and in the composite systems.
00:02:01.370 --> 00:02:08.245
There was a great breakthrough from Japan, and that breakthrough in Japan happened in 1989.
00:02:08.545 --> 00:02:12.481
It was brought to market in 1992, in the United States.
00:02:12.481 --> 00:02:21.525
And that was the introduction of a composite that was somewhere in between, an adhesive of the different bonding systems and the restorative filled composites.
00:02:21.824 --> 00:02:24.293
And that's called the flowable composite.
00:02:24.293 --> 00:02:29.199
Flowable composites had a viscosity that was very easy to spread around.
00:02:29.399 --> 00:02:31.534
There was no problem with it flowing.
00:02:31.534 --> 00:02:33.971
And that's why it's called flowable composite.
00:02:33.971 --> 00:02:38.742
But the filler of the flowable composite to make it more stiff.
00:02:39.076 --> 00:02:40.743
We had a lot of options.
00:02:40.743 --> 00:02:55.091
The option that the first global composite, which came out of Japan to make it stiffer, was to take a composite that was polymerized and grind it up, and went to ground up into small particles and was put in the adhesive resin.
00:02:55.358 --> 00:03:07.437
Then the polymerization was less because the matrix that was polymerization was surrounding these filler particles, and so the shrinkage was reduced in half.
00:03:07.437 --> 00:03:11.574
It went from seven and 8% to three and 4%.
00:03:11.742 --> 00:03:13.509
That was the first innovation.
00:03:13.509 --> 00:03:20.783
But this microfilm floor with those ground up resin particles had more flexibility.
00:03:20.783 --> 00:03:22.151
It had a downside.
00:03:22.151 --> 00:03:34.064
It didn't have any radiopacity It was completely radiolucence So the first flowable it was called Protect liner F, which was part of the Liner bond one system that was introduced in 1989.
00:03:34.064 --> 00:03:49.946
In Japan, in 1992, in the United States, was able to be investigated in 1993 by Bart van Meerbeek, who we referred to last podcast when he reviewed 30 different bonding systems that were available.
00:03:50.079 --> 00:03:56.420
Of those 30 bonding systems, less than a half dozen, maybe 4 or 5 are still marketed in the world.
00:03:56.420 --> 00:04:01.223
So 25 have not been manufactured now because they weren't as popular.
00:04:01.223 --> 00:04:02.358
They didn't work as well.
00:04:02.358 --> 00:04:22.745
But Van Meerbeek when he used this liner, bought one system in his PhD dissertation, saw that it did something very important when it added this layer of filled adhesive, a microfilm filled adhesive on top of the primer and bond that was part of the dental bonding system, photo bond that was in the liner board one system.
00:04:22.745 --> 00:04:37.560
And he found out that this had a characteristic which he called a gradient of M0E, modulus of elasticity, which is a measure of stiffness of a plastic, some plastic flexible, some very stiff.
00:04:37.560 --> 00:04:49.639
But this modest elasticity gradient was a continuation of the gradient that he discovered in the three layers of the hybrid layer, which he called inter diffusionary zones.
00:04:49.639 --> 00:05:06.857
The lowest diffusionary zone, which is the most important, was that gooey encapsulation of water and hema molecules, and that had a very low modulus of elasticity of around 2 or 3 Gigapascals is the measurement of the modulus of elasticity.
00:05:06.857 --> 00:05:35.050
Sometimes it's called Young's modulus, but as the layers of the hybrid layer were investigated with a testing technique which is called a micro indentation technique, Van Meerbeek was able to see it went from 2 to 3 in the lowest the diffusion zone to 3 to 4 in the middle into diffusion free zone, and then it got up to a stiffness of about six in the outer portion of the inner diffusion result.
00:05:35.050 --> 00:05:42.192
And then when the flowable was put on top of it, that brought that up to about 8 or 9 gigapascals.
00:05:42.192 --> 00:05:51.201
And so he had this gradient of stiffness and that gradient of stiffness gave the characteristics of this line or bond system some superiority.
00:05:51.334 --> 00:05:58.475
At that same time, in the early 1990s, experimentations were done in the neighboring country of Belgium.
00:05:58.475 --> 00:06:04.548
Belgium is where van Meerbeek was, but in a neighboring country of Holland and Amsterdam.
00:06:04.548 --> 00:06:14.691
Experimentations were done by Karel Davidson continuing his work of the 1984 87 period, and he had a graduate student that was very bright.
00:06:14.691 --> 00:06:32.509
Her name was Chantal Kemp Schulte, and she published a very important paper in 1990, and that paper in 1990 started to test different types of liners that were being suggested to overcome this problem of sensitivity after restoration with composite fillings.
00:06:32.809 --> 00:06:53.530
Now, the composite feeling sensitivity was a manifestation of shrinkage that pulled the hybrid layer and destroyed the hybrid layer, allowing a gap of bubble fluid to be underneath the restoration when the patient was biting on that, then all of a sudden the fluid went back out of the gap into the pulp, and that hurt.
00:06:53.530 --> 00:07:00.203
That's the hydrodynamic source of pain that Martin Branstromm pioneered ten years earlier, in 1982.
00:07:00.237 --> 00:07:06.877
So Schulte was trying to solve the problem of sensitivity under restorations, composite restorations that had this shrinkage.
00:07:06.877 --> 00:07:14.584
So she tried different liners, and the only liners that worked were composite based resin based liners.
00:07:14.718 --> 00:07:28.031
The glass ionomer that had been introduced, in that same decade had different characteristics, but it did not help with this bond bility, and it didn't help with the sensitivity problem.
00:07:28.131 --> 00:07:38.208
But this idea that the seal was improved by using a resin liner, 1990 confirmed in 1993 by Van Meerbeek.
00:07:38.208 --> 00:07:43.213
Out of two different universities doing good dental research, in vitro dental research.
00:07:43.213 --> 00:07:48.218
When I read that paper, this would have been in 1995, 96 period.
00:07:48.218 --> 00:07:59.162
In my mind, I was starting to think in the terms of how long it takes to do something and how that affected the development of the hybrid layer.
00:07:59.162 --> 00:08:03.300
And this resin, codeine took a little bit longer to do.
00:08:03.300 --> 00:08:12.275
And that was the insight that I believe was the important part of the capsule paper, although it wasn't discussed in those terms.
00:08:12.275 --> 00:08:13.576
But this is the paper.
00:08:13.576 --> 00:08:20.817
And as you go through early papers, there's always questions of, well, why didn't they try this material?
00:08:20.817 --> 00:08:22.185
Why didn't they try this technique?
00:08:22.185 --> 00:08:26.889
But the answer is they're trying to figure out and usually are trying to simplify something.
00:08:26.889 --> 00:08:31.728
So when they introduce a step that takes more time, they're thinking, well, it's kind of a trade off.
00:08:31.728 --> 00:08:33.429
You know I'm going to get less sensitivity.
00:08:33.429 --> 00:08:34.764
It's going to take more time.
00:08:34.764 --> 00:08:40.569
But nobody was really thinking in terms of long term success of mimicking a tooth.
00:08:40.569 --> 00:08:48.912
So the idea of biomimetic in its infancy really wasn't talked in terms of let's try to get a seal as close to a natural tooth as possible.
00:08:48.912 --> 00:09:00.990
But when I read this paper, there was another paper that had influenced me from the very beginning by my second mentor, and that paper was published in 1999.
00:09:00.990 --> 00:09:09.231
And this paper had the title Global Resin Composites as Filled Adhesives, written by Gary Unterbrink and Bill Liebenberg.
00:09:09.264 --> 00:09:14.269
Now, if you understand what that title is saying, you have to understand something about adhesives.
00:09:14.269 --> 00:09:27.149
You have to understand that the first adhesive systems bonded to death and had no filler material, and they were not being used with a global composite, which can have different types of field characteristics microfilmed.
00:09:27.149 --> 00:09:39.262
Or the later the ceramic filled microfilmed composites were basically replaced by the ceramic filled composites, which were called micro hybrid filler floorboards.
00:09:39.262 --> 00:09:43.166
But my second mentor after a lot was Gary Unterbrink.
00:09:43.166 --> 00:09:51.206
I didn't meet him until 1998 at the Ada Convention in San Francisco, and I talked to him for actually a couple of hours.
00:09:51.206 --> 00:09:56.145
It was obvious that Ray Bertolotti’s connection with Gary Unterbrink was very important.
00:09:56.145 --> 00:10:08.792
They were basically talking the same terminology on dental bonding systems, the same terminology on global composites, the same terminology on C factor, which is a new concept to me.
00:10:08.792 --> 00:10:14.464
But I was asking him very specifically about how C factor relates to shrinkage.
00:10:14.831 --> 00:10:22.538
Shrinkage relates to bond strength, how bond strength relates to sensitivity or gaps underneath restorations.
00:10:22.538 --> 00:10:31.548
In these mentoring conversations that I had with Gary in 1998, later in 2000, 2002, 2004, Ray bought a lot.
00:10:31.548 --> 00:10:37.653
He would bring Gary in to bring out the Lake Tahoe to give a lecture a couple of years.
00:10:37.653 --> 00:10:42.491
When he retired, I asked permission if I could use his PowerPoint and he said sure.
00:10:42.491 --> 00:10:48.431
So I got a copy of Gary Unterbrink’s PowerPoint to to take me deeper into the things that he understood.
00:10:48.598 --> 00:10:53.436
And this paper for me, I call it a heuristic paper.
00:10:53.436 --> 00:10:55.772
Heuristic is a scientific term.
00:10:55.772 --> 00:11:07.584
When you study something, it doesn't give you the exact answer of your question, but it teaches you some methods to think about how you might get to an answer of the actual question that a scientist is using.
00:11:07.584 --> 00:11:13.089
And so heuristic methods are methods that help you be a better investigator.
00:11:13.288 --> 00:11:19.528
I read this paper that was published in 1999, in a pre publication form.
00:11:19.629 --> 00:11:22.865
So before you write a paper, there are many drafts.
00:11:22.865 --> 00:11:27.202
The paper that I'm best known for is the paper with Pascal Magne.
00:11:27.202 --> 00:11:30.473
I spent four months full time writing the papers.
00:11:30.473 --> 00:11:35.512
The numerous drafts that Pascal and I would give to each other eventually led to the drafts.
00:11:35.512 --> 00:11:46.723
It went to the Quintessence International, and then we had an editor there that would try to see if there were grammar, grammatical errors, or logical errors that seemed questionable to somebody wasn't familiar with the subject.
00:11:46.723 --> 00:12:02.172
Anyway, these editors can go through 5 or 6, 10 edits, but I did get this last pre-publication edit from Gary Unterbrink in 1998, and so when I read the paper in 1999, I already was very excited about it.
00:12:02.471 --> 00:12:11.815
but the first paragraph that he wrote said this adhesive dentistry could be expressed as a simple relationship between bonds and stress.
00:12:11.815 --> 00:12:17.187
If the bonds can withstand the stress, the restorative technique will be successful.
00:12:17.353 --> 00:12:30.667
So I later when I started to teach in 2003, these concepts of increasing bond rates and decreasing stresses to make a restoration successful, I named this paragraph.
00:12:30.667 --> 00:12:32.969
I called it the adhesive equation.
00:12:32.969 --> 00:12:44.246
I coined the term the piece of equation, and by that time in 2003, I had listed eight different ways to increase bond strengths and ten different ways to decrease stresses.
00:12:44.514 --> 00:12:49.318
Decreasing of stress A stress scene has to do with less than four and less than six.
00:12:49.318 --> 00:13:01.898
Less than four is decreasing polymerization stresses in the first 24 hours of the restorative period, and then less than six is decreasing stresses for the rest of the life as the restoration is chewed on.
00:13:01.898 --> 00:13:03.132
And that's occlusion.
00:13:03.132 --> 00:13:06.469
And so lesson two, lesson for lesson six.
00:13:06.469 --> 00:13:08.837
Those are all decreasing stresses.
00:13:08.837 --> 00:13:09.739
Lesson one.
00:13:09.739 --> 00:13:10.406
Lesson three.
00:13:10.406 --> 00:13:13.408
Lesson five rule increasing bond strength.
00:13:13.408 --> 00:13:21.317
And the culmination of all of my investigations eventually brought me to the point that had been really ignored and overlooked.
00:13:21.317 --> 00:13:40.103
Slightly mentioned a few times by Carol Davidson, it was that whenever we have these restorations polymerization, we have to realize that there's a beginning to the polymerization and there's an ending to the polymerization, and so that eventually led me to the concept that I published decoupling with time.
00:13:40.103 --> 00:13:58.988
And so between Carel Davidson, Kemp Schulte and Gary Unterbrink the idea of decoupling and decoupling with time became the controlling concept that all of the six lessons teach protocols to improve bonds or decrease stresses.
00:13:59.154 --> 00:14:11.567
And so the main problem that was needing to be overcome with the decoupling of time was the hierarchy of bond ability, or the differences in mineralization in each of the hard tissues.
00:14:11.567 --> 00:14:15.104
And I was able to identify six different hard tissues.
00:14:15.104 --> 00:14:23.980
And the scientific literature had been able to tell us how bond strengths could be achieved on these six different levels of mineralization.
00:14:24.180 --> 00:14:37.360
And if we did that, we were able to, with this protocol of decoupling for a certain amount of time, meaning staying thin in the bulk of composites, saying thin in the volume of composite for a certain amount of time.
00:14:37.493 --> 00:14:45.868
Then we had the ability to flow or move all of the molecules towards the hybrid layer, so it did not stress the hybrid layer.
00:14:46.168 --> 00:14:59.081
This idea of immediate didn't ceiling, which has become very common and very talked about in the world of biomimetic dentistry, was obviously first put into play in the world of adhesive dentistry.
00:14:59.081 --> 00:15:14.663
And we've talked about Sato's paper, published in 1994, in Bertsinger’s paper, published in Europe in 1996, Pascal Magne 2005 gave us the actual numbers for immediate didn't ceiling and how it quadrupled the potential bond strength.
00:15:14.663 --> 00:15:18.935
If c factor was controlled and a surface preparation was controlled.
00:15:19.134 --> 00:15:23.605
And of course we had to understand the bond into carious surfaces.
00:15:23.605 --> 00:15:45.628
When I wrote a paper with Pascal, he was very excited that I had all the numbers, scientific investigations on different surfaces, different C factors, and different preparations from the Japanese, and a key paper in 2003 from Van Verbeek that show that air abrasion was a surface conditioning to deal with the smear layer problem.
00:15:45.794 --> 00:15:47.797
My goodness, there's a lot to think about.
00:15:47.797 --> 00:16:04.212
But the bottom line is that this resin coating, once it was understood as an improvement over only immediate in the ceiling, and again, that came with the liner bond system of 1989 1993 time period.
00:16:04.346 --> 00:16:13.523
Then other companies started to make global composites, and the global composites had, very vast differences in fillers.
00:16:13.523 --> 00:16:20.196
Some of the fillers were micron size, the micron versus the submicron filler particles.
00:16:20.529 --> 00:16:22.164
Every company had their own.
00:16:22.164 --> 00:16:23.966
Ours is the best of the best.
00:16:23.966 --> 00:16:32.108
Of course, the only one that had been shown with published in vitro and in vivo research was the global composite came out of Japan.
00:16:32.274 --> 00:16:42.951
Everything else was just copying, and there were lawsuits in the United States because certain companies thought that they had invented globals, when in reality they had been invented in Japan.
00:16:42.951 --> 00:16:49.125
And so companies, United States were suing each other for infringements of ideas that really weren't theirs.
00:16:49.524 --> 00:16:51.461
That's just how the world works.
00:16:53.629 --> 00:16:58.567
But once form of composites became kind of, okay, that's the new thing.
00:16:58.567 --> 00:16:59.701
Yeah, this was good.
00:16:59.701 --> 00:17:18.721
Nobody understood how they were working or what they did or if there is a difference between a formal composite that was a chemical cure for global composite or a light cure, because the transition between light cured, a chemical cure was happening just when flow bubbles were coming into the national and international market.
00:17:18.721 --> 00:17:28.563
There's a huge difference between chemical cure and light cure in the rate of polymerization five times 500% faster with light cure.
00:17:28.798 --> 00:17:31.500
And of course, you know, dentists aren't physicists.
00:17:31.500 --> 00:17:33.401
They're not, you know, engineers.
00:17:33.401 --> 00:17:36.471
They are simple minded people thinking faster is better.
00:17:36.771 --> 00:17:42.377
So the light cure transition became hugely popular in the United States because it was faster.
00:17:42.377 --> 00:17:48.884
Fukuyama, in his so in his 1980 book, was only using chemical cure adhesives.
00:17:49.317 --> 00:17:55.490
And these chemical cure adhesives had chemical cure composites put on top of them.
00:17:55.490 --> 00:18:02.197
It decreased the stress enough that they had long term bond ability in certain cavity preparations.
00:18:02.197 --> 00:18:05.167
Basically class one cavity preparations.
00:18:05.167 --> 00:18:14.042
But then when the Americans started to go and the Europeans started to go on the global composites, the global composites were tested, more system radically.
00:18:14.109 --> 00:18:31.092
And one of the most important papers was done by Dietschi And one of the graduate students, the University of Geneva, tested over 20 different global composites for modulus of elasticity, rate of polymerization, and bond strength to certain adhesives.
00:18:31.092 --> 00:18:41.369
It's very, very difficult to test all combinations of all adhesives with all flowables but Dietschi was basically able to make a few assumptions.
00:18:41.369 --> 00:18:47.509
And those assumptions were if you get a higher margins of elasticity, it was better.
00:18:47.509 --> 00:18:50.512
That's not so easy to do.
00:18:50.645 --> 00:18:53.782
The filler particles have to be in a resin matrix.
00:18:53.782 --> 00:18:56.519
The resin matrix interacts the filler particles.
00:18:56.519 --> 00:19:07.128
If that happens well or doesn't happen well, it actually affects both the bond testing and the long term success of a restoration.
00:19:07.128 --> 00:19:19.574
If it's bonded internally to itself through the silanization of the ceramic particles to the resin matrix, or the polymerization of the resin matrix to the micro filled resin filler particles.
00:19:19.574 --> 00:19:28.750
Again, you know, most dentists don't even want to think about this, but I was driven to figure this out because I was at my ropes.
00:19:28.750 --> 00:19:36.458
end you know, a few years earlier, I quit dentistry out of frustration that these blow bubbles that I use didn't change anything.
00:19:36.458 --> 00:19:37.826
I still had sensitivity.
00:19:37.826 --> 00:19:41.963
I still had teeth becoming root canals, I still had fractures and teeth.
00:19:41.963 --> 00:19:46.868
I was using adhesives, I was using composites, I was using available materials.
00:19:46.868 --> 00:19:50.505
But I didn't really understand the science that was evolved.
00:19:50.605 --> 00:19:56.978
Once I had a ray of light a ray of Ray Bertolotti’s light shined on this problem.
00:19:56.978 --> 00:19:59.681
It inspired me to find another mentor.
00:19:59.681 --> 00:20:02.884
Gary Unterbrink inspired me to find another mentor.
00:20:03.118 --> 00:20:13.361
Didier Dietschi You know, in those years, from 1995 to 2000, I understood that there is much science and that science needs to be integrated.
00:20:13.361 --> 00:20:20.201
It wasn't going to be one material's going to solve all your problems, or one technique is going to solve all your problems.
00:20:20.201 --> 00:20:26.841
It had to be an integration based on understanding of polymerization dynamics of these composite materials.
00:20:27.342 --> 00:20:33.281
After we got that figured out, after testing it for five years in my office, I said, okay, I got this. Figure it out.
00:20:33.281 --> 00:20:34.516
Now what are we going to do with it?
00:20:34.516 --> 00:20:36.117
You know, we can keep being a dentist.
00:20:36.117 --> 00:20:37.552
That would have made us a lot more money.
00:20:37.552 --> 00:20:47.896
But the bottom line is that when I decided to start teaching, obviously I had to have dentists that could understand that resin coating is part of decoupling with time.
00:20:47.996 --> 00:20:55.670
In other words, the time it takes you to put resin at a half millimeter thickness on top of your dental bonding system.
00:20:55.870 --> 00:21:00.375
It's doing something very important, more than the importance of the flowable.
00:21:00.375 --> 00:21:04.946
It's allowing the polymerization of the dental bonding system to take place.
00:21:04.946 --> 00:21:08.416
It takes a minute and a half to put on your flow and polymerize it.
00:21:08.416 --> 00:21:19.227
During that minute a half good things are happening as far as the Hema hydrogel formation in these three into diffusionary zones of your hybrid layer.
00:21:19.361 --> 00:21:28.336
And so once that was firmly in, in my mind, and I started to teach that in 2003 to other dentists, then we came on.
00:21:28.336 --> 00:21:34.008
The next breakthrough was what is the next layer on top of your resin coating?
00:21:34.175 --> 00:21:35.777
Again, it's going to be a resin.
00:21:35.777 --> 00:21:37.645
And how thick could it be?
00:21:37.645 --> 00:21:47.188
Or what material would be ideal to still have the flow of the resin molecules as they polymerize into monomer?
00:21:47.188 --> 00:22:02.103
Small polymers, larger polymers that movement as long as it's in one direction, then there's no stress that stretches the hybrid layer and can even debond the hybrid layer in the first few minutes of the restorative process.
00:22:02.103 --> 00:22:07.976
And so that hybrid layer, once we understood the resin coating, was absolutely essential.
00:22:07.976 --> 00:22:09.411
The question is how thick?
00:22:09.411 --> 00:22:16.851
Because the thickness we know if it got to two millimeters, then you'd have a 50% degradation of the hybrid layer.
00:22:16.951 --> 00:22:24.659
You know, that exact number didn't come out until 2004, but I'd already figured that out independently based on the science.
00:22:24.659 --> 00:22:31.032
And so in the paper from Nikolaenko was published in the first year that we were teaching the six lessons approach.
00:22:31.132 --> 00:22:35.236
I immediately put it into the the articles that we had the doctors read.
00:22:35.437 --> 00:22:43.511
We started in 2003, was 20 articles, and then we went to 22, and then we went to 25, and then we went to 27.
00:22:43.578 --> 00:22:48.149
And at 27, I could see that, you know, I probably couldn't help myself.
00:22:48.149 --> 00:22:51.152
Eventually the doctors would have to learn a hundred articles.
00:22:51.419 --> 00:22:59.627
But, you know, for 99% of the dentists in the world, if we can just tell them what to do and how to do it, that's going to be enough.
00:22:59.861 --> 00:23:01.696
They don't need to know how to teach it.
00:23:01.696 --> 00:23:14.542
But when we started to teach the mastership program five years ago, I was kind of tired of just teaching the cookbook and and knowing that many doctors would still have problems in difficult cases.
00:23:14.542 --> 00:23:22.917
And so I made a decision to start teaching these advanced concepts to dentists who were motivated to know more than just what to do.
00:23:22.917 --> 00:23:24.886
They wanted to know why it worked.
00:23:24.886 --> 00:23:30.058
And the resin coating worked because it was part of decoupling with time.
00:23:30.058 --> 00:23:33.862
The next layer, as long as it's thin, less than one millimeter.
00:23:33.862 --> 00:23:38.132
And of course, Simone de la Perry pioneered that in 2002.
00:23:38.166 --> 00:23:46.074
As long as that volume is in what we call micro cofactor increments, then there's no damage to the hybrid layer.
00:23:46.074 --> 00:23:47.141
How thick can you go?
00:23:47.141 --> 00:23:53.681
Well, you can go one millimeter thicker after the half millimeter that you've placed on your dental bonding system.
00:23:53.681 --> 00:24:08.963
So the Alleman Deliperi rule is don't get thicker than 1.5mm of composite during the first five minutes of the polymerization reaction that was started with your polymerization of the resin of your dental bonding system.
00:24:09.365 --> 00:24:11.232
Okay, there's more.
00:24:13.001 --> 00:24:33.221
This resin coating in a vital tooth is critical to make sure that we don't have a transformation of fluid underneath the hybrid layer, because when we get close to a pulp horn, particularly on a molar, then the pulp of fluid is being pumped every heartbeat into the bonding field.
00:24:33.321 --> 00:24:39.661
And if you take too much time to get the polymerization done, then you can have fluid.
00:24:39.827 --> 00:24:47.735
And that fluid gets bonded into the restoration as a sealed gap of fluid under the restoration that causes sensitivity.
00:24:47.735 --> 00:24:56.945
This can particularly happen when you're close to a popcorn and you have a thin adhesive layer in your dental bonding system.
00:24:56.945 --> 00:25:03.451
Dental bonding systems have adhesive layer anywhere from ten microns to 80 microns.
00:25:03.551 --> 00:25:13.795
The thickest dental adhesive in dental bonding systems, or up to bond ethyl all bond three and PCU one from three different companies.
00:25:13.795 --> 00:25:34.616
The thinnest or almost universal easily manufactured because most early investigators were talking about bonding to enamel, and they wanted a strong bond to enamel, and they could get that with a very thin layer that wouldn't have the problem of pooling, which also which always increase the polymerization shrinkage.
00:25:34.616 --> 00:25:42.657
If you have too much of an unfilled adhesive, which are the thin adhesives, then that unfilled adhesive, that pool shrinks a lot.
00:25:42.657 --> 00:25:46.561
And that's where a gap will be more prone to to form.
00:25:46.661 --> 00:25:55.269
And so the thin adhesives that are good on enamel are terrible on dentin because there is a transmutation pumping against them.
00:25:55.570 --> 00:26:00.041
It bends that adhesive to even less than ten microns.
00:26:00.341 --> 00:26:15.823
If you have an adhesive layer that is less than ten microns, there is enough air in the ambient environment to inhibit the polymerization from the free radical initiator, which is called camphor quinone.
00:26:15.823 --> 00:26:24.565
Camphor quinone, when it hits oxygen, is unstable and it cannot then form free radicals well.
00:26:24.599 --> 00:26:31.406
This oxygen inhibition was recognized for 100 years from people that worked with plastics all the time.
00:26:31.539 --> 00:26:48.690
And that oxygen inhibition layer, if you added some composite on top of it, wasn't a problem because the new layer of composite when it polymerize would diffuse free radicals and the free radical oligomers into that on polymerize monomer layer.
00:26:48.690 --> 00:26:59.033
And they would polymerize from the top to the bottom rather than coming out of the the layer that was polymerize underneath the oxygen inhibited layer.
00:26:59.100 --> 00:27:04.839
So this diffusion polymerization happened whether the oxygen inhibited layer was there or not there beyond.
00:27:04.839 --> 00:27:09.510
So did some very good experimentations in the 90s on this.
00:27:09.977 --> 00:27:16.350
it showed that the arch inhibited layer wasn't didn't have anything to do with whether composites polymerized well with each other.
00:27:16.350 --> 00:27:19.821
But there was, you know, myths about that.
00:27:20.021 --> 00:27:26.828
And so you hear in dental students vocabulary conversations all the time how you need an oxygen inhibited layer to polymerize.
00:27:26.828 --> 00:27:28.229
It's just not true.
00:27:28.229 --> 00:27:38.473
That problem of transmutation coming from the bottom and oxygen inhibition coming from the top means that if you get too thin when you put the light on it, it doesn't polymerize at all.
00:27:38.473 --> 00:27:40.141
It's totally inhibited.
00:27:40.141 --> 00:27:47.849
And so you think that you've got a layer of adhesive adhesive for your body system sealing the dental tubules.
00:27:47.849 --> 00:27:58.426
But the air inhibition in this situation completely means that it's not polymerize at all until the next layer is put on, which usually is a global composite. Now.
00:27:58.526 --> 00:28:08.469
But if you do not understand that this is a problem and this is a problem, then you have that UN polymerized layer of your dental bonding system.
00:28:08.469 --> 00:28:17.712
Well, that problem can be solved by making the adhesive thicker so the translation can't poke little holes into 80 microns.
00:28:17.712 --> 00:28:20.681
It can only get up maybe 20 microns or 35.
00:28:20.982 --> 00:28:24.786
So these thicker adhesive layers like off to one fell.
00:28:24.819 --> 00:28:27.188
The NFL stands for filled.
00:28:27.188 --> 00:28:31.692
And that filled means that it went from ten microns to 80 microns.
00:28:31.959 --> 00:28:47.642
It was a very, important improvement that Al Kobashigawa made for Kerr company, the only three real field adhesives that overcome this idea of air inhibition and partially solve the problem of transudation.
00:28:47.675 --> 00:28:54.148
Two of those have the problem of being one bottle systems, which we will talk about in another lecture.
00:28:54.148 --> 00:29:12.000
When we understand that we have this ability with the resin coating to make sure that that in that adhesive layer polymerize is even if it's been pounded with purple fluid coming out this thick, as this layer of resin code is going to be 500 microns, you can't ever inhibit 500 microns.
00:29:12.000 --> 00:29:16.604
There's only, maybe 30 or 40 on top if you are thin of global.
00:29:16.604 --> 00:29:28.983
But if you air thin, billet piece of layer of your dental bonding system, then you get to that ten micron layer, which can be mean that you won't get any polymerization with the light at the initial light.
00:29:28.983 --> 00:29:30.184
Curing stage.
00:29:30.184 --> 00:29:30.751
Okay.
00:29:30.751 --> 00:29:34.455
So you know, we've had some pretty big ideas.
00:29:34.722 --> 00:29:39.227
The immediate dentin sealing should always be thought of in conjunction with resin coating.
00:29:39.327 --> 00:29:46.133
Somebody in systems have the ability to handle resin coating at the same time that they are forming the hybrid layer.
00:29:46.133 --> 00:29:51.939
But two of the three have a problem of the hybrid layer now becomes contaminate dated with solvents.
00:29:51.939 --> 00:30:03.551
And so these systems that are one model, universal systems that have one model, always have a contamination of solvents that interfere with a full polymerization of the monomers.
00:30:03.751 --> 00:30:13.094
And so you always will have a 30% reduction of your bond strength when you mix the priming elements that are hydrophilic with the bonding elements that are hydrophobic.
00:30:13.094 --> 00:30:14.962
So we do not recommend those.
00:30:14.962 --> 00:30:19.467
But it's always like, well, in my country I can't get this, I can't get this.
00:30:19.467 --> 00:30:25.173
I understand if you have to use a one bottle system, then what would you do not like cure it?
00:30:25.206 --> 00:30:35.750
You would add another layer of your one bottle system, another bottle layer of the adhesive, or another flushable immediately, and light cure those both at the same time.
00:30:35.750 --> 00:30:41.122
It's a it's it's a technique that has been tried and it does have some improvement.
00:30:41.122 --> 00:30:45.059
But the real answer to the problem is to find a two bottle system.
00:30:45.059 --> 00:30:59.440
If you have two bottle systems, that's your first indication that the manufacturer understands these problems of hydrophobicity makes you have purple fluid versus hydrophobicity, which is bonding with your restorative composites on top.
00:30:59.440 --> 00:31:06.514
And so those are the manufactures that are, you know, saying dentists are smart enough to understand this even at a basic level.
00:31:06.514 --> 00:31:10.151
So let's make products that they can get really excited about.
00:31:10.284 --> 00:31:11.086
Okay.
00:31:11.086 --> 00:31:14.088
Well that's our number 12.
00:31:14.288 --> 00:31:18.326
So we're very glad I think that's going to finish our first season.
00:31:18.693 --> 00:31:24.699
So our first season of the Six Lessons podcast is now in the can, as they say.
00:31:25.032 --> 00:31:27.702
Enjoy, get bonded, stay bonded.
00:00:26.275 --> 00:00:30.179
Welcome to episode 12 of the Six Lessons podcast.
00:00:30.446 --> 00:00:34.250
Today we're going to be talking about a topic near and dear to my heart.
00:00:34.384 --> 00:00:35.918
Resin coating.
00:00:35.918 --> 00:00:47.263
Resin coating is a concept that doesn't get as much respect as it should in the world of adhesive dentistry, all of the products that we use are resin based.
00:00:47.631 --> 00:00:50.766
The resin idea is a polymerized molecule.
00:00:50.766 --> 00:00:55.371
Resins can be very stiff or they can be very flexible.
00:00:55.371 --> 00:00:59.475
For example, soft contact lenses that has a monomer called Hema.
00:00:59.842 --> 00:01:02.778
The Hema is a water loving molecule.
00:01:02.778 --> 00:01:07.751
It's very small, so it's very flexible, but it also adapts well with water.
00:01:07.783 --> 00:01:19.128
Now, harder plastics like these lenses of my glasses, they have a polymerization that is much more complex and it does not like water at all.
00:01:19.128 --> 00:01:21.731
So that's a hydrophobic situation.
00:01:21.731 --> 00:01:27.871
In the composites we use, the resins have a combination of hydrophilic and hydrophobic.
00:01:27.871 --> 00:01:30.039
In the dental bonding systems.
00:01:30.039 --> 00:01:38.981
And the dental bonding systems have to connect to hydrophobic resins that are in what we call the restorative composite aspect.
00:01:38.981 --> 00:01:55.932
But in between the dental bonding system and the restorative materials that we use, which are composites, we need to understand that there has been a tremendous amount of experimentation and that experimentation has been both in the bonding systems and in the composite systems.
00:02:01.370 --> 00:02:08.245
There was a great breakthrough from Japan, and that breakthrough in Japan happened in 1989.
00:02:08.545 --> 00:02:12.481
It was brought to market in 1992, in the United States.
00:02:12.481 --> 00:02:21.525
And that was the introduction of a composite that was somewhere in between, an adhesive of the different bonding systems and the restorative filled composites.
00:02:21.824 --> 00:02:24.293
And that's called the flowable composite.
00:02:24.293 --> 00:02:29.199
Flowable composites had a viscosity that was very easy to spread around.
00:02:29.399 --> 00:02:31.534
There was no problem with it flowing.
00:02:31.534 --> 00:02:33.971
And that's why it's called flowable composite.
00:02:33.971 --> 00:02:38.742
But the filler of the flowable composite to make it more stiff.
00:02:39.076 --> 00:02:40.743
We had a lot of options.
00:02:40.743 --> 00:02:55.091
The option that the first global composite, which came out of Japan to make it stiffer, was to take a composite that was polymerized and grind it up, and went to ground up into small particles and was put in the adhesive resin.
00:02:55.358 --> 00:03:07.437
Then the polymerization was less because the matrix that was polymerization was surrounding these filler particles, and so the shrinkage was reduced in half.
00:03:07.437 --> 00:03:11.574
It went from seven and 8% to three and 4%.
00:03:11.742 --> 00:03:13.509
That was the first innovation.
00:03:13.509 --> 00:03:20.783
But this microfilm floor with those ground up resin particles had more flexibility.
00:03:20.783 --> 00:03:22.151
It had a downside.
00:03:22.151 --> 00:03:34.064
It didn't have any radiopacity It was completely radiolucence So the first flowable it was called Protect liner F, which was part of the Liner bond one system that was introduced in 1989.
00:03:34.064 --> 00:03:49.946
In Japan, in 1992, in the United States, was able to be investigated in 1993 by Bart van Meerbeek, who we referred to last podcast when he reviewed 30 different bonding systems that were available.
00:03:50.079 --> 00:03:56.420
Of those 30 bonding systems, less than a half dozen, maybe 4 or 5 are still marketed in the world.
00:03:56.420 --> 00:04:01.223
So 25 have not been manufactured now because they weren't as popular.
00:04:01.223 --> 00:04:02.358
They didn't work as well.
00:04:02.358 --> 00:04:22.745
But Van Meerbeek when he used this liner, bought one system in his PhD dissertation, saw that it did something very important when it added this layer of filled adhesive, a microfilm filled adhesive on top of the primer and bond that was part of the dental bonding system, photo bond that was in the liner board one system.
00:04:22.745 --> 00:04:37.560
And he found out that this had a characteristic which he called a gradient of M0E, modulus of elasticity, which is a measure of stiffness of a plastic, some plastic flexible, some very stiff.
00:04:37.560 --> 00:04:49.639
But this modest elasticity gradient was a continuation of the gradient that he discovered in the three layers of the hybrid layer, which he called inter diffusionary zones.
00:04:49.639 --> 00:05:06.857
The lowest diffusionary zone, which is the most important, was that gooey encapsulation of water and hema molecules, and that had a very low modulus of elasticity of around 2 or 3 Gigapascals is the measurement of the modulus of elasticity.
00:05:06.857 --> 00:05:35.050
Sometimes it's called Young's modulus, but as the layers of the hybrid layer were investigated with a testing technique which is called a micro indentation technique, Van Meerbeek was able to see it went from 2 to 3 in the lowest the diffusion zone to 3 to 4 in the middle into diffusion free zone, and then it got up to a stiffness of about six in the outer portion of the inner diffusion result.
00:05:35.050 --> 00:05:42.192
And then when the flowable was put on top of it, that brought that up to about 8 or 9 gigapascals.
00:05:42.192 --> 00:05:51.201
And so he had this gradient of stiffness and that gradient of stiffness gave the characteristics of this line or bond system some superiority.
00:05:51.334 --> 00:05:58.475
At that same time, in the early 1990s, experimentations were done in the neighboring country of Belgium.
00:05:58.475 --> 00:06:04.548
Belgium is where van Meerbeek was, but in a neighboring country of Holland and Amsterdam.
00:06:04.548 --> 00:06:14.691
Experimentations were done by Karel Davidson continuing his work of the 1984 87 period, and he had a graduate student that was very bright.
00:06:14.691 --> 00:06:32.509
Her name was Chantal Kemp Schulte, and she published a very important paper in 1990, and that paper in 1990 started to test different types of liners that were being suggested to overcome this problem of sensitivity after restoration with composite fillings.
00:06:32.809 --> 00:06:53.530
Now, the composite feeling sensitivity was a manifestation of shrinkage that pulled the hybrid layer and destroyed the hybrid layer, allowing a gap of bubble fluid to be underneath the restoration when the patient was biting on that, then all of a sudden the fluid went back out of the gap into the pulp, and that hurt.
00:06:53.530 --> 00:07:00.203
That's the hydrodynamic source of pain that Martin Branstromm pioneered ten years earlier, in 1982.
00:07:00.237 --> 00:07:06.877
So Schulte was trying to solve the problem of sensitivity under restorations, composite restorations that had this shrinkage.
00:07:06.877 --> 00:07:14.584
So she tried different liners, and the only liners that worked were composite based resin based liners.
00:07:14.718 --> 00:07:28.031
The glass ionomer that had been introduced, in that same decade had different characteristics, but it did not help with this bond bility, and it didn't help with the sensitivity problem.
00:07:28.131 --> 00:07:38.208
But this idea that the seal was improved by using a resin liner, 1990 confirmed in 1993 by Van Meerbeek.
00:07:38.208 --> 00:07:43.213
Out of two different universities doing good dental research, in vitro dental research.
00:07:43.213 --> 00:07:48.218
When I read that paper, this would have been in 1995, 96 period.
00:07:48.218 --> 00:07:59.162
In my mind, I was starting to think in the terms of how long it takes to do something and how that affected the development of the hybrid layer.
00:07:59.162 --> 00:08:03.300
And this resin, codeine took a little bit longer to do.
00:08:03.300 --> 00:08:12.275
And that was the insight that I believe was the important part of the capsule paper, although it wasn't discussed in those terms.
00:08:12.275 --> 00:08:13.576
But this is the paper.
00:08:13.576 --> 00:08:20.817
And as you go through early papers, there's always questions of, well, why didn't they try this material?
00:08:20.817 --> 00:08:22.185
Why didn't they try this technique?
00:08:22.185 --> 00:08:26.889
But the answer is they're trying to figure out and usually are trying to simplify something.
00:08:26.889 --> 00:08:31.728
So when they introduce a step that takes more time, they're thinking, well, it's kind of a trade off.
00:08:31.728 --> 00:08:33.429
You know I'm going to get less sensitivity.
00:08:33.429 --> 00:08:34.764
It's going to take more time.
00:08:34.764 --> 00:08:40.569
But nobody was really thinking in terms of long term success of mimicking a tooth.
00:08:40.569 --> 00:08:48.912
So the idea of biomimetic in its infancy really wasn't talked in terms of let's try to get a seal as close to a natural tooth as possible.
00:08:48.912 --> 00:09:00.990
But when I read this paper, there was another paper that had influenced me from the very beginning by my second mentor, and that paper was published in 1999.
00:09:00.990 --> 00:09:09.231
And this paper had the title Global Resin Composites as Filled Adhesives, written by Gary Unterbrink and Bill Liebenberg.
00:09:09.264 --> 00:09:14.269
Now, if you understand what that title is saying, you have to understand something about adhesives.
00:09:14.269 --> 00:09:27.149
You have to understand that the first adhesive systems bonded to death and had no filler material, and they were not being used with a global composite, which can have different types of field characteristics microfilmed.
00:09:27.149 --> 00:09:39.262
Or the later the ceramic filled microfilmed composites were basically replaced by the ceramic filled composites, which were called micro hybrid filler floorboards.
00:09:39.262 --> 00:09:43.166
But my second mentor after a lot was Gary Unterbrink.
00:09:43.166 --> 00:09:51.206
I didn't meet him until 1998 at the Ada Convention in San Francisco, and I talked to him for actually a couple of hours.
00:09:51.206 --> 00:09:56.145
It was obvious that Ray Bertolotti’s connection with Gary Unterbrink was very important.
00:09:56.145 --> 00:10:08.792
They were basically talking the same terminology on dental bonding systems, the same terminology on global composites, the same terminology on C factor, which is a new concept to me.
00:10:08.792 --> 00:10:14.464
But I was asking him very specifically about how C factor relates to shrinkage.
00:10:14.831 --> 00:10:22.538
Shrinkage relates to bond strength, how bond strength relates to sensitivity or gaps underneath restorations.
00:10:22.538 --> 00:10:31.548
In these mentoring conversations that I had with Gary in 1998, later in 2000, 2002, 2004, Ray bought a lot.
00:10:31.548 --> 00:10:37.653
He would bring Gary in to bring out the Lake Tahoe to give a lecture a couple of years.
00:10:37.653 --> 00:10:42.491
When he retired, I asked permission if I could use his PowerPoint and he said sure.
00:10:42.491 --> 00:10:48.431
So I got a copy of Gary Unterbrink’s PowerPoint to to take me deeper into the things that he understood.
00:10:48.598 --> 00:10:53.436
And this paper for me, I call it a heuristic paper.
00:10:53.436 --> 00:10:55.772
Heuristic is a scientific term.
00:10:55.772 --> 00:11:07.584
When you study something, it doesn't give you the exact answer of your question, but it teaches you some methods to think about how you might get to an answer of the actual question that a scientist is using.
00:11:07.584 --> 00:11:13.089
And so heuristic methods are methods that help you be a better investigator.
00:11:13.288 --> 00:11:19.528
I read this paper that was published in 1999, in a pre publication form.
00:11:19.629 --> 00:11:22.865
So before you write a paper, there are many drafts.
00:11:22.865 --> 00:11:27.202
The paper that I'm best known for is the paper with Pascal Magne.
00:11:27.202 --> 00:11:30.473
I spent four months full time writing the papers.
00:11:30.473 --> 00:11:35.512
The numerous drafts that Pascal and I would give to each other eventually led to the drafts.
00:11:35.512 --> 00:11:46.723
It went to the Quintessence International, and then we had an editor there that would try to see if there were grammar, grammatical errors, or logical errors that seemed questionable to somebody wasn't familiar with the subject.
00:11:46.723 --> 00:12:02.172
Anyway, these editors can go through 5 or 6, 10 edits, but I did get this last pre-publication edit from Gary Unterbrink in 1998, and so when I read the paper in 1999, I already was very excited about it.
00:12:02.471 --> 00:12:11.815
but the first paragraph that he wrote said this adhesive dentistry could be expressed as a simple relationship between bonds and stress.
00:12:11.815 --> 00:12:17.187
If the bonds can withstand the stress, the restorative technique will be successful.
00:12:17.353 --> 00:12:30.667
So I later when I started to teach in 2003, these concepts of increasing bond rates and decreasing stresses to make a restoration successful, I named this paragraph.
00:12:30.667 --> 00:12:32.969
I called it the adhesive equation.
00:12:32.969 --> 00:12:44.246
I coined the term the piece of equation, and by that time in 2003, I had listed eight different ways to increase bond strengths and ten different ways to decrease stresses.
00:12:44.514 --> 00:12:49.318
Decreasing of stress A stress scene has to do with less than four and less than six.
00:12:49.318 --> 00:13:01.898
Less than four is decreasing polymerization stresses in the first 24 hours of the restorative period, and then less than six is decreasing stresses for the rest of the life as the restoration is chewed on.
00:13:01.898 --> 00:13:03.132
And that's occlusion.
00:13:03.132 --> 00:13:06.469
And so lesson two, lesson for lesson six.
00:13:06.469 --> 00:13:08.837
Those are all decreasing stresses.
00:13:08.837 --> 00:13:09.739
Lesson one.
00:13:09.739 --> 00:13:10.406
Lesson three.
00:13:10.406 --> 00:13:13.408
Lesson five rule increasing bond strength.
00:13:13.408 --> 00:13:21.317
And the culmination of all of my investigations eventually brought me to the point that had been really ignored and overlooked.
00:13:21.317 --> 00:13:40.103
Slightly mentioned a few times by Carol Davidson, it was that whenever we have these restorations polymerization, we have to realize that there's a beginning to the polymerization and there's an ending to the polymerization, and so that eventually led me to the concept that I published decoupling with time.
00:13:40.103 --> 00:13:58.988
And so between Carel Davidson, Kemp Schulte and Gary Unterbrink the idea of decoupling and decoupling with time became the controlling concept that all of the six lessons teach protocols to improve bonds or decrease stresses.
00:13:59.154 --> 00:14:11.567
And so the main problem that was needing to be overcome with the decoupling of time was the hierarchy of bond ability, or the differences in mineralization in each of the hard tissues.
00:14:11.567 --> 00:14:15.104
And I was able to identify six different hard tissues.
00:14:15.104 --> 00:14:23.980
And the scientific literature had been able to tell us how bond strengths could be achieved on these six different levels of mineralization.
00:14:24.180 --> 00:14:37.360
And if we did that, we were able to, with this protocol of decoupling for a certain amount of time, meaning staying thin in the bulk of composites, saying thin in the volume of composite for a certain amount of time.
00:14:37.493 --> 00:14:45.868
Then we had the ability to flow or move all of the molecules towards the hybrid layer, so it did not stress the hybrid layer.
00:14:46.168 --> 00:14:59.081
This idea of immediate didn't ceiling, which has become very common and very talked about in the world of biomimetic dentistry, was obviously first put into play in the world of adhesive dentistry.
00:14:59.081 --> 00:15:14.663
And we've talked about Sato's paper, published in 1994, in Bertsinger’s paper, published in Europe in 1996, Pascal Magne 2005 gave us the actual numbers for immediate didn't ceiling and how it quadrupled the potential bond strength.
00:15:14.663 --> 00:15:18.935
If c factor was controlled and a surface preparation was controlled.
00:15:19.134 --> 00:15:23.605
And of course we had to understand the bond into carious surfaces.
00:15:23.605 --> 00:15:45.628
When I wrote a paper with Pascal, he was very excited that I had all the numbers, scientific investigations on different surfaces, different C factors, and different preparations from the Japanese, and a key paper in 2003 from Van Verbeek that show that air abrasion was a surface conditioning to deal with the smear layer problem.
00:15:45.794 --> 00:15:47.797
My goodness, there's a lot to think about.
00:15:47.797 --> 00:16:04.212
But the bottom line is that this resin coating, once it was understood as an improvement over only immediate in the ceiling, and again, that came with the liner bond system of 1989 1993 time period.
00:16:04.346 --> 00:16:13.523
Then other companies started to make global composites, and the global composites had, very vast differences in fillers.
00:16:13.523 --> 00:16:20.196
Some of the fillers were micron size, the micron versus the submicron filler particles.
00:16:20.529 --> 00:16:22.164
Every company had their own.
00:16:22.164 --> 00:16:23.966
Ours is the best of the best.
00:16:23.966 --> 00:16:32.108
Of course, the only one that had been shown with published in vitro and in vivo research was the global composite came out of Japan.
00:16:32.274 --> 00:16:42.951
Everything else was just copying, and there were lawsuits in the United States because certain companies thought that they had invented globals, when in reality they had been invented in Japan.
00:16:42.951 --> 00:16:49.125
And so companies, United States were suing each other for infringements of ideas that really weren't theirs.
00:16:49.524 --> 00:16:51.461
That's just how the world works.
00:16:53.629 --> 00:16:58.567
But once form of composites became kind of, okay, that's the new thing.
00:16:58.567 --> 00:16:59.701
Yeah, this was good.
00:16:59.701 --> 00:17:18.721
Nobody understood how they were working or what they did or if there is a difference between a formal composite that was a chemical cure for global composite or a light cure, because the transition between light cured, a chemical cure was happening just when flow bubbles were coming into the national and international market.
00:17:18.721 --> 00:17:28.563
There's a huge difference between chemical cure and light cure in the rate of polymerization five times 500% faster with light cure.
00:17:28.798 --> 00:17:31.500
And of course, you know, dentists aren't physicists.
00:17:31.500 --> 00:17:33.401
They're not, you know, engineers.
00:17:33.401 --> 00:17:36.471
They are simple minded people thinking faster is better.
00:17:36.771 --> 00:17:42.377
So the light cure transition became hugely popular in the United States because it was faster.
00:17:42.377 --> 00:17:48.884
Fukuyama, in his so in his 1980 book, was only using chemical cure adhesives.
00:17:49.317 --> 00:17:55.490
And these chemical cure adhesives had chemical cure composites put on top of them.
00:17:55.490 --> 00:18:02.197
It decreased the stress enough that they had long term bond ability in certain cavity preparations.
00:18:02.197 --> 00:18:05.167
Basically class one cavity preparations.
00:18:05.167 --> 00:18:14.042
But then when the Americans started to go and the Europeans started to go on the global composites, the global composites were tested, more system radically.
00:18:14.109 --> 00:18:31.092
And one of the most important papers was done by Dietschi And one of the graduate students, the University of Geneva, tested over 20 different global composites for modulus of elasticity, rate of polymerization, and bond strength to certain adhesives.
00:18:31.092 --> 00:18:41.369
It's very, very difficult to test all combinations of all adhesives with all flowables but Dietschi was basically able to make a few assumptions.
00:18:41.369 --> 00:18:47.509
And those assumptions were if you get a higher margins of elasticity, it was better.
00:18:47.509 --> 00:18:50.512
That's not so easy to do.
00:18:50.645 --> 00:18:53.782
The filler particles have to be in a resin matrix.
00:18:53.782 --> 00:18:56.519
The resin matrix interacts the filler particles.
00:18:56.519 --> 00:19:07.128
If that happens well or doesn't happen well, it actually affects both the bond testing and the long term success of a restoration.
00:19:07.128 --> 00:19:19.574
If it's bonded internally to itself through the silanization of the ceramic particles to the resin matrix, or the polymerization of the resin matrix to the micro filled resin filler particles.
00:19:19.574 --> 00:19:28.750
Again, you know, most dentists don't even want to think about this, but I was driven to figure this out because I was at my ropes.
00:19:28.750 --> 00:19:36.458
end you know, a few years earlier, I quit dentistry out of frustration that these blow bubbles that I use didn't change anything.
00:19:36.458 --> 00:19:37.826
I still had sensitivity.
00:19:37.826 --> 00:19:41.963
I still had teeth becoming root canals, I still had fractures and teeth.
00:19:41.963 --> 00:19:46.868
I was using adhesives, I was using composites, I was using available materials.
00:19:46.868 --> 00:19:50.505
But I didn't really understand the science that was evolved.
00:19:50.605 --> 00:19:56.978
Once I had a ray of light a ray of Ray Bertolotti’s light shined on this problem.
00:19:56.978 --> 00:19:59.681
It inspired me to find another mentor.
00:19:59.681 --> 00:20:02.884
Gary Unterbrink inspired me to find another mentor.
00:20:03.118 --> 00:20:13.361
Didier Dietschi You know, in those years, from 1995 to 2000, I understood that there is much science and that science needs to be integrated.
00:20:13.361 --> 00:20:20.201
It wasn't going to be one material's going to solve all your problems, or one technique is going to solve all your problems.
00:20:20.201 --> 00:20:26.841
It had to be an integration based on understanding of polymerization dynamics of these composite materials.
00:20:27.342 --> 00:20:33.281
After we got that figured out, after testing it for five years in my office, I said, okay, I got this. Figure it out.
00:20:33.281 --> 00:20:34.516
Now what are we going to do with it?
00:20:34.516 --> 00:20:36.117
You know, we can keep being a dentist.
00:20:36.117 --> 00:20:37.552
That would have made us a lot more money.
00:20:37.552 --> 00:20:47.896
But the bottom line is that when I decided to start teaching, obviously I had to have dentists that could understand that resin coating is part of decoupling with time.
00:20:47.996 --> 00:20:55.670
In other words, the time it takes you to put resin at a half millimeter thickness on top of your dental bonding system.
00:20:55.870 --> 00:21:00.375
It's doing something very important, more than the importance of the flowable.
00:21:00.375 --> 00:21:04.946
It's allowing the polymerization of the dental bonding system to take place.
00:21:04.946 --> 00:21:08.416
It takes a minute and a half to put on your flow and polymerize it.
00:21:08.416 --> 00:21:19.227
During that minute a half good things are happening as far as the Hema hydrogel formation in these three into diffusionary zones of your hybrid layer.
00:21:19.361 --> 00:21:28.336
And so once that was firmly in, in my mind, and I started to teach that in 2003 to other dentists, then we came on.
00:21:28.336 --> 00:21:34.008
The next breakthrough was what is the next layer on top of your resin coating?
00:21:34.175 --> 00:21:35.777
Again, it's going to be a resin.
00:21:35.777 --> 00:21:37.645
And how thick could it be?
00:21:37.645 --> 00:21:47.188
Or what material would be ideal to still have the flow of the resin molecules as they polymerize into monomer?
00:21:47.188 --> 00:22:02.103
Small polymers, larger polymers that movement as long as it's in one direction, then there's no stress that stretches the hybrid layer and can even debond the hybrid layer in the first few minutes of the restorative process.
00:22:02.103 --> 00:22:07.976
And so that hybrid layer, once we understood the resin coating, was absolutely essential.
00:22:07.976 --> 00:22:09.411
The question is how thick?
00:22:09.411 --> 00:22:16.851
Because the thickness we know if it got to two millimeters, then you'd have a 50% degradation of the hybrid layer.
00:22:16.951 --> 00:22:24.659
You know, that exact number didn't come out until 2004, but I'd already figured that out independently based on the science.
00:22:24.659 --> 00:22:31.032
And so in the paper from Nikolaenko was published in the first year that we were teaching the six lessons approach.
00:22:31.132 --> 00:22:35.236
I immediately put it into the the articles that we had the doctors read.
00:22:35.437 --> 00:22:43.511
We started in 2003, was 20 articles, and then we went to 22, and then we went to 25, and then we went to 27.
00:22:43.578 --> 00:22:48.149
And at 27, I could see that, you know, I probably couldn't help myself.
00:22:48.149 --> 00:22:51.152
Eventually the doctors would have to learn a hundred articles.
00:22:51.419 --> 00:22:59.627
But, you know, for 99% of the dentists in the world, if we can just tell them what to do and how to do it, that's going to be enough.
00:22:59.861 --> 00:23:01.696
They don't need to know how to teach it.
00:23:01.696 --> 00:23:14.542
But when we started to teach the mastership program five years ago, I was kind of tired of just teaching the cookbook and and knowing that many doctors would still have problems in difficult cases.
00:23:14.542 --> 00:23:22.917
And so I made a decision to start teaching these advanced concepts to dentists who were motivated to know more than just what to do.
00:23:22.917 --> 00:23:24.886
They wanted to know why it worked.
00:23:24.886 --> 00:23:30.058
And the resin coating worked because it was part of decoupling with time.
00:23:30.058 --> 00:23:33.862
The next layer, as long as it's thin, less than one millimeter.
00:23:33.862 --> 00:23:38.132
And of course, Simone de la Perry pioneered that in 2002.
00:23:38.166 --> 00:23:46.074
As long as that volume is in what we call micro cofactor increments, then there's no damage to the hybrid layer.
00:23:46.074 --> 00:23:47.141
How thick can you go?
00:23:47.141 --> 00:23:53.681
Well, you can go one millimeter thicker after the half millimeter that you've placed on your dental bonding system.
00:23:53.681 --> 00:24:08.963
So the Alleman Deliperi rule is don't get thicker than 1.5mm of composite during the first five minutes of the polymerization reaction that was started with your polymerization of the resin of your dental bonding system.
00:24:09.365 --> 00:24:11.232
Okay, there's more.
00:24:13.001 --> 00:24:33.221
This resin coating in a vital tooth is critical to make sure that we don't have a transformation of fluid underneath the hybrid layer, because when we get close to a pulp horn, particularly on a molar, then the pulp of fluid is being pumped every heartbeat into the bonding field.
00:24:33.321 --> 00:24:39.661
And if you take too much time to get the polymerization done, then you can have fluid.
00:24:39.827 --> 00:24:47.735
And that fluid gets bonded into the restoration as a sealed gap of fluid under the restoration that causes sensitivity.
00:24:47.735 --> 00:24:56.945
This can particularly happen when you're close to a popcorn and you have a thin adhesive layer in your dental bonding system.
00:24:56.945 --> 00:25:03.451
Dental bonding systems have adhesive layer anywhere from ten microns to 80 microns.
00:25:03.551 --> 00:25:13.795
The thickest dental adhesive in dental bonding systems, or up to bond ethyl all bond three and PCU one from three different companies.
00:25:13.795 --> 00:25:34.616
The thinnest or almost universal easily manufactured because most early investigators were talking about bonding to enamel, and they wanted a strong bond to enamel, and they could get that with a very thin layer that wouldn't have the problem of pooling, which also which always increase the polymerization shrinkage.
00:25:34.616 --> 00:25:42.657
If you have too much of an unfilled adhesive, which are the thin adhesives, then that unfilled adhesive, that pool shrinks a lot.
00:25:42.657 --> 00:25:46.561
And that's where a gap will be more prone to to form.
00:25:46.661 --> 00:25:55.269
And so the thin adhesives that are good on enamel are terrible on dentin because there is a transmutation pumping against them.
00:25:55.570 --> 00:26:00.041
It bends that adhesive to even less than ten microns.
00:26:00.341 --> 00:26:15.823
If you have an adhesive layer that is less than ten microns, there is enough air in the ambient environment to inhibit the polymerization from the free radical initiator, which is called camphor quinone.
00:26:15.823 --> 00:26:24.565
Camphor quinone, when it hits oxygen, is unstable and it cannot then form free radicals well.
00:26:24.599 --> 00:26:31.406
This oxygen inhibition was recognized for 100 years from people that worked with plastics all the time.
00:26:31.539 --> 00:26:48.690
And that oxygen inhibition layer, if you added some composite on top of it, wasn't a problem because the new layer of composite when it polymerize would diffuse free radicals and the free radical oligomers into that on polymerize monomer layer.
00:26:48.690 --> 00:26:59.033
And they would polymerize from the top to the bottom rather than coming out of the the layer that was polymerize underneath the oxygen inhibited layer.
00:26:59.100 --> 00:27:04.839
So this diffusion polymerization happened whether the oxygen inhibited layer was there or not there beyond.
00:27:04.839 --> 00:27:09.510
So did some very good experimentations in the 90s on this.
00:27:09.977 --> 00:27:16.350
it showed that the arch inhibited layer wasn't didn't have anything to do with whether composites polymerized well with each other.
00:27:16.350 --> 00:27:19.821
But there was, you know, myths about that.
00:27:20.021 --> 00:27:26.828
And so you hear in dental students vocabulary conversations all the time how you need an oxygen inhibited layer to polymerize.
00:27:26.828 --> 00:27:28.229
It's just not true.
00:27:28.229 --> 00:27:38.473
That problem of transmutation coming from the bottom and oxygen inhibition coming from the top means that if you get too thin when you put the light on it, it doesn't polymerize at all.
00:27:38.473 --> 00:27:40.141
It's totally inhibited.
00:27:40.141 --> 00:27:47.849
And so you think that you've got a layer of adhesive adhesive for your body system sealing the dental tubules.
00:27:47.849 --> 00:27:58.426
But the air inhibition in this situation completely means that it's not polymerize at all until the next layer is put on, which usually is a global composite. Now.
00:27:58.526 --> 00:28:08.469
But if you do not understand that this is a problem and this is a problem, then you have that UN polymerized layer of your dental bonding system.
00:28:08.469 --> 00:28:17.712
Well, that problem can be solved by making the adhesive thicker so the translation can't poke little holes into 80 microns.
00:28:17.712 --> 00:28:20.681
It can only get up maybe 20 microns or 35.
00:28:20.982 --> 00:28:24.786
So these thicker adhesive layers like off to one fell.
00:28:24.819 --> 00:28:27.188
The NFL stands for filled.
00:28:27.188 --> 00:28:31.692
And that filled means that it went from ten microns to 80 microns.
00:28:31.959 --> 00:28:47.642
It was a very, important improvement that Al Kobashigawa made for Kerr company, the only three real field adhesives that overcome this idea of air inhibition and partially solve the problem of transudation.
00:28:47.675 --> 00:28:54.148
Two of those have the problem of being one bottle systems, which we will talk about in another lecture.
00:28:54.148 --> 00:29:12.000
When we understand that we have this ability with the resin coating to make sure that that in that adhesive layer polymerize is even if it's been pounded with purple fluid coming out this thick, as this layer of resin code is going to be 500 microns, you can't ever inhibit 500 microns.
00:29:12.000 --> 00:29:16.604
There's only, maybe 30 or 40 on top if you are thin of global.
00:29:16.604 --> 00:29:28.983
But if you air thin, billet piece of layer of your dental bonding system, then you get to that ten micron layer, which can be mean that you won't get any polymerization with the light at the initial light.
00:29:28.983 --> 00:29:30.184
Curing stage.
00:29:30.184 --> 00:29:30.751
Okay.
00:29:30.751 --> 00:29:34.455
So you know, we've had some pretty big ideas.
00:29:34.722 --> 00:29:39.227
The immediate dentin sealing should always be thought of in conjunction with resin coating.
00:29:39.327 --> 00:29:46.133
Somebody in systems have the ability to handle resin coating at the same time that they are forming the hybrid layer.
00:29:46.133 --> 00:29:51.939
But two of the three have a problem of the hybrid layer now becomes contaminate dated with solvents.
00:29:51.939 --> 00:30:03.551
And so these systems that are one model, universal systems that have one model, always have a contamination of solvents that interfere with a full polymerization of the monomers.
00:30:03.751 --> 00:30:13.094
And so you always will have a 30% reduction of your bond strength when you mix the priming elements that are hydrophilic with the bonding elements that are hydrophobic.
00:30:13.094 --> 00:30:14.962
So we do not recommend those.
00:30:14.962 --> 00:30:19.467
But it's always like, well, in my country I can't get this, I can't get this.
00:30:19.467 --> 00:30:25.173
I understand if you have to use a one bottle system, then what would you do not like cure it?
00:30:25.206 --> 00:30:35.750
You would add another layer of your one bottle system, another bottle layer of the adhesive, or another flushable immediately, and light cure those both at the same time.
00:30:35.750 --> 00:30:41.122
It's a it's it's a technique that has been tried and it does have some improvement.
00:30:41.122 --> 00:30:45.059
But the real answer to the problem is to find a two bottle system.
00:30:45.059 --> 00:30:59.440
If you have two bottle systems, that's your first indication that the manufacturer understands these problems of hydrophobicity makes you have purple fluid versus hydrophobicity, which is bonding with your restorative composites on top.
00:30:59.440 --> 00:31:06.514
And so those are the manufactures that are, you know, saying dentists are smart enough to understand this even at a basic level.
00:31:06.514 --> 00:31:10.151
So let's make products that they can get really excited about.
00:31:10.284 --> 00:31:11.086
Okay.
00:31:11.086 --> 00:31:14.088
Well that's our number 12.
00:31:14.288 --> 00:31:18.326
So we're very glad I think that's going to finish our first season.
00:31:18.693 --> 00:31:24.699
So our first season of the Six Lessons podcast is now in the can, as they say.
00:31:25.032 --> 00:31:27.702
Enjoy, get bonded, stay bonded.